无机胶凝体系对水泥基饰面砂浆性能影响的研究
作者:潘伟,段瑜芳
[瓦克化学(中国)有限公司,上海 200233]
摘要:研究了不同掺量的无水石膏和β-半水石膏在不同胶凝材料用量下,对饰面砂浆力学性能、吸水量和抗泛碱的影响。结果表明:石膏掺量较低时,砂浆的抗折和抗压强度较高、吸水量较低、抗泛碱效果较好,但拉伸强度较低;同等掺量时,掺加无水石膏的砂浆抗折和抗压强度较高。
关键词:饰面砂浆;无水石膏;β-半水石膏;泛碱
中图分类号:TU564;TQ177.6 文献标识码:A 文章编号:1001-702X(2017)04-0009-04
关键词:饰面砂浆;无水石膏;β-半水石膏;泛碱
中图分类号:TU564;TQ177.6 文献标识码:A 文章编号:1001-702X(2017)04-0009-04
Study on influence of inorganic binder system on performance of cement based decorative mortar
PAN Wei,DUAN Yufang
[Wacker Chemicals(China) Co. Ltd.,Shanghai 200233,China]
PAN Wei,DUAN Yufang
[Wacker Chemicals(China) Co. Ltd.,Shanghai 200233,China]
Abstract:In the paper,under different binders' content,the influence of different dosage of anhydrite and β-hemihydrate on mechanical performance,water adsorption amount and anti-efflorescence are studied. The test results show that,with lower gypsum dosage,the flexural and compressive strength of mortar was high,water adsorption amount was low,and anti-efflorescence effect was good,while the tensile adhesive strength was lower;on the same dosage,flexural and compressive strength of mortar with anhydrite addition was higher.
Key words:decorative mortar,anhydrite,β-hemihydrate,efflorescence