树脂基料对超薄型钢结构防火涂料性能的影响
作者:刘德红,刘芝君,王振,张逸超,李之锋
(江西理工大学 材料科学与工程学院,江西 赣州 341000)
摘要:分别采用苯丙乳液、硅丙乳液和聚醋酸乙烯酯乳液作为树脂基料,制备了水性超薄型钢结构防火涂料,研究了乳液种类对防火涂料理化性能及耐火性能的影响,并研究了乳液用量对防火涂料耐火性能的影响。研究表明,采用聚醋酸乙烯酯乳液为树脂基料,且当乳液质量在体系中占32%时,防火涂料的耐火性能最优。
关键词:钢结构;防火涂料;树脂基料;聚醋酸乙烯酯乳液
中图分类号:TU56+1.66 文献标识码:A 文章编号:1001-702X(2018)01-0037-03
Effects of resin binder on the ultra-thin fire resistive coating for steel structure
LIU Dehong,LIU Zhijun,WANG Zhen,ZHANG Yichao,LI Zhifeng
(School of Material Science and Engineering,Jiangxi University of Science and Technology,Ganzhou 341000,China)
LIU Dehong,LIU Zhijun,WANG Zhen,ZHANG Yichao,LI Zhifeng
(School of Material Science and Engineering,Jiangxi University of Science and Technology,Ganzhou 341000,China)
Abstract:The water-based ultra-thin fire resistive coating for steel structure was prepared by using styrene-acrylic emulsion,silicone-acrylic emulsion and polyvinyl acetate emulsion as the resin binder respectively. This paper studied the effect of the type of emulsion on the physical properties and fire-resistant property of fire resistive coating. Then studied the effect of different content of polyvinyl acetate emulsion on fire-resistant property of fire resistive coating. The results show that,using polyvinyl acetate emulsion as the resin binder when the content of polyvinyl acetate emulsion is 32% by mass,the fire resistive coating has the best fire-resistant property.
Key words:steel structure,fire resistive coating,resin binder,polyvinyl acetate emulsion